Dhruv Metals, Hyderabad, produces precision Aluminium Hex Bars and Rods in common alloys like 6061, 5052, and 7075. Cut to accurate hexagonal profiles with CNC-grade surface finish, they meet ASTM B211/B221 specifications providing excellent machinability and aesthetic surface finish. Hex bars are appropriate for mechanical fasteners, ornamental structural supports, and architectural hardware that calls for simple machining. Dhruv Metals offers hex bars in specific lengths, polish conditions, and anodized finishes. Their precise cross-section reduces material waste and machining time to fulfill requirements of accurate geometry and finish.
6061 hex bars (Mg-Si) yield tensile ~310 MPa, yield ~270 MPa, elongation 12–17%. 5052 bars (Mg-Cr) yield tensile ~260–330 MPa, yield ~193 MPa, elongation ~12–20%. 7075 bars yield tensile ~570 MPa and yield ~500 MPa, elongation ~11–13%. These bars are cold- or hot-finished, heat treatable (T6), and hold dimensional accuracy. Surface finish and hex form are perfect for turning bolts, fasteners, and precision components. Good corrosion resistance and formability enable trustworthy machining and anodizing processes.
Standards : ASTM B221, B211, B565, B316, AMS 4121 2014
Temper : O
Standard : ASTM, ASME, AMS, GB/T, JIS
Length : 1000-6000
Size : 5 mm To 500 mm
Diameter : 6-150
Finish : Bright, Polish & Black
Type : Hot-Rolled (HR) / Cold-Rolled (CR) Sheet
| Alloy | Fe | Si | Mg | Mn | Cu | Zn | Ti | Cr | Others | AI |
| 1100 (min) | 0.35 | 0.25 | 0.01 | 0.01 | 0.05 | 0.01 | 0.020 | Trace | 0.05 (each) | 99.60% |
| 1100 (max) | 0.50 | 0.35 | 0.03 | 0.05 | 0.20 | 0.05 | 0.030 | Trace | 0.15 (total) | remainder |
| 5083 | 0.40 max | 0.40 max | 4.0 / 4.90 | 0.40 / 1.0 | 0.10 max | 0.25 max | 0.15 max | 0.05 / 0.25 | 0.05 max | Bal |
| 6061 | 0.7 | 0.4-0.8 | 0.8-1.2 | 0.15 | 0.15-0.4 | 0.25 | 0.15 | 0.15-0.35 | 0.005/0.15 | Remainder |
| 6068 | 0.50 max | 0.7 – 1.3 | 0.06-1.20 | 0.40-1.00 | 0.10 max | 0.20 max | 0.10 max | 0.25 max | 0.05 max | Bal |
| 7075 min | 2.10 | 1.20 | 5.10 | 0.18 | ||||||
| 7075 max | 0.50 | 0.40 | 2.90 | 0.30 | 2.00 | 6.10 | 0.20 | 0.28 | 0.05 |
| Alloy | Temper | UTS(Mpa) | % Elongation | Tensile Strength | Hardness Brinell | Proof Stress | Yield Strength (PSI) | Shear Strength (PSI) | Brinell Hardness | |||
| Min | Max | 0.5 mm -0.8 mm | 0.81 mm – 1.30 mm | 1.30 mm – above | ||||||||
| 1100 | O | 75 | 110 | 20 | 25 | 29 | ||||||
| H12 | 95 | 130 | 5 | 6 | 7 | |||||||
| H14 | 110 | 145 | 3 | 4 | 5 | |||||||
| H16 | 130 | 165 | 2 | 3 | 4 | |||||||
| H18 | 150 | — | 2 | 2 | 3 | |||||||
| 5083 | 12 Min % | 275 – 350 MPa | 75 HB | 125 Min MPa | ||||||||
| 6061 | – | 45,000 | 12 | 40,000 | 31,000 | 95 | ||||||
| 6082 | 8 | 295 | 95 | – | 240 | – | – | |||||
| 7075 T6, T651 | 11 | 83-572 | 73- 503 | 150 | ||||||||
| 7075 T73, T7351 | 13 | 73-503 | 63-434 | NA | ||||||||
| Grade | UNS | USA | Japan | France | ISO | WNR | EN | DIN | ISO | BS (OLD) |
| 1100 | A91100 | AA1100 | JIS A1100P | NF 1100 | Al 99.0 Cu. | – | – | – | – | – |
| 6082 | A96082 | AA6082 | – | – | – | 3.2315 | AW-6082 | AlMgSi1 | AlSi1MgMn | HE30 |
| 5083 | A95083 | 5083 | – | – | AlMg4,5Mn0,7 | 3.3547 | AW-AlMg4,5Mn0,7 | AlMg4,5Mn | – | – |
| 6061 | A96061 | AA6061 | – | – | – | 3.3211 | AW-AlMg1SiCu EN AW-6061 | AlMgSiCu | AlMg1SiCu | HE20 |
| 7075 | A97075 | 7075 | 3.4365 | ENAW-AlZn5.5MgCu EN AW-7075 | AlZnMgCu1.5 | AlZn6MgCu | 7075 L95 L96, V95 |
| HEXAGONS | ||
| Size(mm) | WT PER FEET IN KGS | WT PER MTR IN KGS |
| 16 | 0.55 | 1.79 |
| 18 | 0.69 | 2.27 |
| 20 | 0.85 | 2.80 |
| 22 | 1.03 | 3.39 |
| 25 | 1.33 | 4.38 |
| 28 | 1.67 | 5.49 |
| 30 | 1.92 | 6.30 |
| 32 | 2.19 | 7.17 |
| 36 | 2.77 | 9.07 |
| 38 | 3.08 | 10.11 |
| 40 | 3.41 | 11.20 |
| 45 | 4.32 | 14.18 |
| 50 | 5.34 | 17.50 |
| 56 | – | – |
| 60 | – | – |
| 65 | – | – |
| 70 | – | – |
| 75 | – | – |
| 80 | – | – |
| 90 | – | – |
| 100 | – | – |
Aluminium hex bar/rod is commonly used in aerospace, automotive, marine, construction, and manufacturing industries for lightweight structures, electrical components, fasteners, and precision machining due to its strength and corrosion resistance.
Aluminum hex bars are produced through extrusion, casting, or forging, followed by heat treatment and machining. This process enhances strength, dimensional accuracy, and surface finish, ensuring consistent quality and performance.
Yes, aluminum hex bar/rod can be welded. Recommended techniques include Tungsten Inert Gas (TIG) welding for precision, and Metal Inert Gas (MIG) welding for faster, more robust welds.
Aluminium Hex Bars and Rods are used for nuts, bolts, machine fasteners, fittings, and ornamental architectural hardware. For manufacturing, they are milled into mechanical couplings, drive couplings, and gear blanks. They are utilized by aerospace and defense industries in precision fittings, mounting spindles, and structural brackets. They are used as bases for knobs and fixtures for tooling. Their decorative finish is perfect for interior trims, furniture hardware, and sign hardware. Dhruv Metals supplies hex bars ready to machine, minimizing scrap and maximizing productivity.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Dhruv Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Hyderabad , India
Copyright 2024 Dhruv Metals. All rights reserved