Dhruv Metals in Hyderabad manufactures accurate Carbon Steel Bright Bars and Rods with features such as a smooth surface finish, close dimensional tolerances, and high mechanical performance. Cold- or hot-finished bars made to ASTM A108/A29 grades such as 1018, 1045, and 1050 provide high machinability, weldability, and straightness for precision engineering. Having bright finishes (ground or peeled), they are utilized in tooling and component manufacture. Dhruv Metals provides round, hex, square, and flat profile bars and rods ready for machining, forming, or broaching applications demanding accuracy and wear resistance.
Bright bars of grades such as 1018 and 1045 have 0.18–0.50% C, 0.3–1.3% Mn, and minute S/P. Tensile strength is 440–640 MPa; yield strength approximately 275–500 MPa; elongation approximately 12–18%. Bright-finish improves fatigue performance. Their cold-drawn or turned finish offers high concentricity and low elongation upon load. The microstructure provides consistent dimensional stability and hardness. These can be surface-hardened or plated due to moderate wear resistance and machinability. Bright bars have precision maintained in tolerance-sensitive applications when subjected to thermal and mechanical stress.
Carbon Steel Bright Square Bar Size: 4 to 100mm
Steel Low Carbon Bright Hex Bar Sizes : 2 to 100 mm A/F
Medium Carbon Steel Bright Angle Bar Size : 3*20*20~12*100*100 mm
Quenching High Carbon Steel Billet Sizes : 1/2″ – 495 mm Dia
Killed Carbon Steel Bright Cold Drawn Bar Processing : Bar cutting to 650mm
Plain Carbon Steel Section Bar Size Range : 3 to 12 mm thickness
| Carbon Steel Grades | C | Mn | Si | S Max. | P Max. |
|---|---|---|---|---|---|
| Ck 45 | 0.42/0.50 | 0.50/0.80 | 0.15/0.35 | 0.04 | 0.04 |
| Ck 55 | 0.52/0.60 | 0.60/0.90 | 0.15/0.35 | 0.04 | 0.04 |
| Ck 60 | 0.57/0.65 | 0.60/0.90 | 0.15/0.35 | 0.04 | 0.04 |
| SAE1006 | 0.08 max | 0.25/0.40 | 0.10/0.30 | 0.05 | 0.04 |
| SAE1008 | 0.10 max | 0.30/0.50 | 0.10/0.30 | 0.05 | 0.04 |
| SAE1010 | 0.08/0.13 | 0.30/0.60 | 0.10/0.30 | 0.05 | 0.04 |
| SAE1018 | 0.15/0.20 | 0.60/0.90 | 0.10/0.30 | 0.05 | 0.04 |
| SAE1020 | 0.18/0.23 | 0.30/0.60 | 0.10/0.30 | 0.09 | 0.04 |
| SAE1030 | 0.28/0.34 | 0.60/0.90 | 0.10/0.40 | 0.05 | 0.04 |
| SAE1035 | 0.32/0.38 | 0.60/0.90 | 0.10/0.40 | 0.05 | 0.04 |
| SAE1040 | 0.37/0.44 | 0.60/0.90 | 0.10/0.40 | 0.05 | 0.04 |
| SAE1045 | 0.40/0.50 | 0.60/0.90 | 0.10/0.40 | 0.05 | 0.04 |
| En-8D | 0.40/0.45 | 0.70/0.90 | 0.05/0.35 | 0.06 | 0.06 |
| En-9 | 0.50/0.60 | 0.50/0.80 | 0.05/0.35 | 0.06 | 0.06 |
| Grade | Yield Strength, | Tensile Strength, | Elongation at Break (in 50 mm) | Bulk Modulus (typical for steel) | Modulus of Elasticity | HBW | Poissons Ratio | Fatigue strength coefficient, of (Mpa) | Shear Modulus | Impacting Energy | Reduction of area, min: |
|---|---|---|---|---|---|---|---|---|---|---|---|
| a36 | 250 MPa | 400 – 550 MPa | 23.00% | 140 GPa | 200 GPa | 0.26 | 79.3 GPa | ||||
| 36300 psi | 58000 – 79800 psi | 23.00% | 20300 ksi | 29000 ksi | 0.26 | 11500 ksi | |||||
| EN45 | 35 (241) | 80 (551) | 40% | 204 Gpa | 948 | ≥63 | |||||
| EN19 | ≥930 Mpa | ≥1080 Mpa | ≥12 | 217 | ≥45 | ||||||
| 105 | 36,000 psi [250 MPa] | 70,000 psi (485 MPa] | 187 | 30% min | |||||||
| EN8 | ≥210 | ≥380 | ≥25 | ≤111HB | ≥50 |
Yes, carbon steel bright bars can attract magnets. Carbon steel is generally magnetic due to its iron content, which exhibits magnetic properties when in a solid, non-alloyed form.
Carbon steel bright bars and rods come in various grades, including mild steel, medium carbon steel, high carbon steel, alloy steel, and tool steel. These types vary in strength, hardness, and flexibility.
Yes, carbon steel bright bars can be recycled after use. The recycling process involves melting down the material, removing impurities, and then reusing it to produce new steel products.
Carbon Steel Bright Bars and Rods have applications in shafts, spindles, gears, bolts, dowels, and machine tool parts. Their smooth finish and close tolerances are appropriate for automated assembly, precision fixtures, and bearing shafts. In automobiles and elevator fields, they‘re employed as axles, crankshafts, and press pins. In manufacturing applications, they‘re used in broaching tools, mechanical support rods, and industrial hardware. Their uniform profile allows them to be suitable for pneumatic/hydraulic valves, pinions, and roller shafts. Dhruv Metals provides bright bars ready for high-volume, precision work.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Dhruv Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Hyderabad , India
Copyright 2024 Dhruv Metals. All rights reserved